Tuning Room-Temperature Magnetism in 2D Materials Through Dielectric Interfaces

by NANOSENSORS
28 October 202628 October 2026
News & Events, Science & Technology

Five-panel arrangement of AFM topography, MFM and KPFM measurements of Fe₃GeTe₂ nanosheets on 50 nm SiOₓ, comparing dark conditions and UV illumination.

Two-dimensional materials have attracted considerable research interest because their properties can differ markedly from those of their bulk counterparts, opening up possibilities for new electronic… Read More »Tuning Room-Temperature Magnetism in 2D Materials Through Dielectric Interfaces

Magnetic Skyrmions in a Thickness Tunable 2D Ferromagnet from a Defect Driven Dzyaloshinskii–Moriya Interaction

by NANOSENSORS
23 September 202215 March 2023
Science & Technology

Figure 4 from “Magnetic Skyrmions in a Thickness Tunable 2D Ferromagnet from a Defect Driven Dzyaloshinskii–Moriya Interaction” by Anirban Chakraborty et al. Thickness dependence of skyrmion size in lamella L2 as imaged by MFM. a) SEM image of the wedge-shaped lamella. The thickness of the lamella varies from ≈100 nm to ≈2 µm. b) MFM image of skyrmions in the lamella at 100 K and 0.032 T. c–f) Evolution of skyrmions as the field is increased from 0.1 to 0.2 T and finally reaches the field polarized state at ≈0.3 T. The blue and red contrast in the MFM images represent up- and down-magnetized domains. All MFM images are at the same scale: a scale bar is shown in (b). g) Skyrmion diameter as a function of lamella thickness including both MFM and LTEM data. NANOSENSORS SSS-MFMR AFM probes for magnetic force microscopy were used for all MFM measurements.

There is considerable interest in van der Waals (vdW) materials as potential hosts for chiral skyrmionic spin textures. Of particular interest is the ferromagnetic, metallic… Read More »Magnetic Skyrmions in a Thickness Tunable 2D Ferromagnet from a Defect Driven Dzyaloshinskii–Moriya Interaction